Chloroprene Rubber

Product parameters
Type Grade Mooney Viscosity Crystallization Rate Characteristics Main Application
General CR121 CR1211 30-45 Medium Good tear and flexural resistance Conveyor belt,ribbed belt, timing belt, cable sheath, etc
CR1212 46-60
CR232 CR2321 35-45 Good weatherability, high loading For making light-colored rubber products, such as seals, dust caps, rubber rollers, liners, rubber dams and hose sheath etc
CR2322 46-55
CR232 High Viscosity According to customers' requirement
CR322 CR3221 30-45 Good tear resistance and excellent dynamic mechanical properties Conveyor belt, hoses,
cable sheath, etc
CR3222 46-60
Remarks:
① Mooney Viscosity:ML(1+4)100℃
Type Grade Mooney Viscosity Crystallization Rate Characteristics Main Application
Special DCR114 DCR1141 30-45 Slow Good low-temperature resistance Mainly used in cold areas of conveyor belt, ribbed belt, timing belt, and cable sheath, etc
DCR1142 46-60
DCR213 DCR2131 35-45 Good weatherability and low-temperature resistance Mainly used in cold areas of dust caps, road and bridge shock pad, sealing strip and other products
DCR2132 46-55
DCR213 High Viscosity According to customers' requirement
Remarks:
① Mooney Viscosity:ML(1+4)100℃
Type Grade Brook Field Viscosity Crystallization Rate Characteristics Main Application
Adhesive Application CR244 CR2441 25-34 Fast Good bonding strength For bonding and self-bonding between rubber, leather, fiber, metal, wood and cement products, etc.
CR2442 35-53
CR2443 54-75
CR2444 76-115
CR244HVA 116-140
CR244HVB ≥141
CR248 CR2481 1000-3000 It can be grafted and copolymerized with MMA, BA and other active monomers to improve the bonding strength For bonding and self-bonding between rubber, leather, fiber, metal, wood and cement products, etc.
CR2482 3001-6000
Remarks:
② Brook Field Viscosity: mPa·s (25℃,5% Toluene solution)
③ Brook Field Viscosity: mPa·s (25℃,15% Toluene solution)